Epoxy grouting material (three components) 
 Product Description 
 Epoxy grouting material, including A (resin) and B (curing agent), C (fill) three components, the product of high quality resin and refined packing, 100% solids, does not contain harmful solvents and other volatile substances . Three components in each group of materials contained in the completely mixed at room temperature can be used without additional ingredients. 
 Product Use 
 1 for the installation of compressors, pumps, punching machine, grinder, ball mill, high-vibration equipment secondary grouting. 
 2 for the grouting of equipment foundation area susceptible to chemical attack. 
 3, for the track based on the bridge support seat by the strong pressure region grouting. 
 For anchors, reinforced planting and construction of structural concrete reinforcement. 
 For concrete, stone, steel, wood and other surfaces to use as a self-leveling mortar. 
 6, for iron, iron rod, rod of steel connections. 
 Features 
 1, high strength, early strength 
 Much better than the compressive strength of cement-based materials, bonded mechanical properties, higher early strength. 
 2, low exothermic peak 
 Can provide up to 120 minutes (25 ° C) hours of operation, suitable for the grouting of large volume use. 
 3, no shrinkage 
 Make sure that the final shape of the grout layer of bearing surface contact, to ensure high-precision equipment installation. 
 4, excellent creep resistance 
 Epoxy grouting material at -50 ° C to +80 ° C for a long time freezing and thawing alternately harsh physical conditions of the vibration pressure on long-term use without plastic deformation to ensure long-term accurate equipment positioning. 
 5, the remarkable resilience 
 Epoxy grouting material can be resolved by moving equipment delivery to any possible move of cement-based grout layer burst load. 
 6, the corrosion resistance of 
 Acid, alkali, salt, grease and other chemicals can withstand long-term exposure to corrosion. 
 Performance indicators (A + B): C ≈ 1:6 
 Compressive strength: 1d> 50MPa, 3d> 65MPa, 7d> 95MPa, and ultimately> 100MPa 
 Flexural strength: 1> 10MPa, 3d> 15MPa, 7d> 20MPa, the final> 25MPa 
 Pullout strength: 1> 8MPa, 3d> 12MPa, 7d> 15MPa, and ultimately> 17MPa 
 Compression elastic membrane: 7d> 18000MPa final> 18500MPa 
 Linear shrinkage: 7d <0.012%, the final <0.012% 
 Exothermic peak <42 ° C 
 Compression creep <1.0 * 10-3mm/mm (180 days) 
 Thermal expansion coefficient of <40 the * 10-6mm/mm / ° C (the molding ,0-60 ° C, 28 days) 
 Note: 
 1, Preheat, molding and conservation in the 23 ± 2 ° C, relative humidity 50 ± 5% under the experimental conditions, other conditions in accordance with appropriate standards. 
 2, the final data at 23 ± 2 ℃ molding and conservation of 7 days, and then accelerated curing at 60 ℃ measured after 6 hours. 
 Product packaging 
 A material iron drums 15kg plastic bucket / barrel B material 45kg barrel / C feed paper plastic compound bag 40kg / bag weight mix ratio (A + B): C = 1:6, each 420 kg net